电压对微弧氧化膜抑制7050铝合金氢脆敏感性的影响

为进一步探究微弧氧化膜和7050铝合金的氢脆敏感性之间的关系,采用了湿空气中的慢应变速率拉伸、拉伸断口形貌分析、微弧氧化试样表面形貌分析及氢含量测试等表征手段,验证了微弧氧化膜抑制7050铝合金在湿空气中发生氢脆的机制。结果表明,不同微弧氧化电压下制备的膜层对7050铝合金具有不同的抑制氢脆效果,抑制机制主要由膜阻氢进入试样和膜致附加压应力两个方面组成。     

铝电解预焙阳极脱落原因分析及对策

国内某电解铝企业电解槽频繁出现脱极现象,脱极率一度达到5%,造成原铝9970率大幅下降,阳极毛耗、氟盐单耗上升,电流效率下降,生产经营指标严重下滑。本文从残极炭碗状况、残极高度、磷铁环状况、磷铁成分、铁炭压降等几个方面进行观测,并对这些现象与脱极之间存在的因果关系进行分析,制定对策加以改进,最后得以扭转。     

Investigation on low-temperature sintered AlN nanoceramics with high thermal conductivity

The aim of this research was to investigate the effect of sintering additive and relatively low-sintering temperature on the thermal conductivity of aluminum nitride nanoceramic. While using nanosized AlN powder and liquid-phase sintering additives, the various sintering processes were performed at temperatures 1400 and 1500°C for several hours. In the analysis methods, thermal conductivity (K) and thermal diffusivity (α) were measured using thermal conductivity analyzer (Hot Disk), scanning electron microscope (SEM) was used to observe the surface morphology of the microstructure, x-ray diffraction analyzer (XRD) to analyze the grain size and crystal structure, Raman spectroscopy (Raman) emission spectrum was analyzed to identify the material microstructure and the densities of AlN specimens were measured by Archimedes method. It was found that the thermal conductivity is related to the densification of nanosize low-temperature sintered material, which can be controlled by additives and sintering temperature. With Y₂O₃ sintering add, the densification of AlN for low-temperature sintering increased by the factor of ～5% to ～12%, and the thermal conductivity was enhanced by 25%. The relative density observed in this research is about 78%-84%, and the thermal conductivity measured is in the range of 9-14 W/mK.     

6061铝合金均匀化过程中AlMnSi弥散颗粒的析出尺寸对再结晶行为的影响

利用力学性能测试、光学显微镜、扫描电镜、透射电镜和能谱分析技术等手段研究了均匀化过程中AlMnSi弥散颗粒的析出尺寸对6061铝合金再结晶行为的影响。结果表明:AlMnSi弥散颗粒在均匀化过程中沿着铝基体[001]晶带轴析出长大,晶体结构为体心立方结构。随着均匀化温度的升高,弥散颗粒的析出尺寸逐渐增大,当AlMnSi弥散颗粒平均尺寸由0.07 μm增长到0.42 μm,最大尺寸由0.21 μm增大到1.12 μm时,力学性能则是先升高后降低。6061铝合金T6态组织仍为变形组织;AlMnSi弥散颗粒尺寸增大到1.12 μm,6061合金T6态组织中出现粗大再结晶,力学性能急剧降低。     

An evaluation of Acacia mearnsii tannin as an aluminum corrosion inhibitor in acid,alkaline, and neutral media

The electrochemical behavior of aluminum in tannin from Acacia mearnsii bark was evaluated by potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS) in media under three different pH conditions: acid, alkaline, and neutral. A relationship among pH, polymerization grade (PG), zeta potential, surface, and electrochemical properties was observed in the inhibition performance of the tannin. At high pH, the oligomer structure of the tannin was affected, resulting in a low PG (4) and high zeta potential (−75 mV), and consequently, the inhibition efficiency decreased (68%) in comparison with that in acid (99%) and neutral media (96%). The values obtained indicate a physisorption mechanism for the aluminum corrosion inhibition in the studied conditions.     

变形铝合金表面锆基化学转化膜的研究现状

化学转化膜是金属表面主要的处理方法之一，具备良好的附着力和耐蚀性，能为铝合金提供一定的临时防护。传统的六价铬酸盐化学转化膜在日渐严苛的环保压力下已经逐渐淘汰，取而代之的是近几年发展迅猛的三价铬及无铬锆基化学转化膜。铝合金可分为铸造铝合金和变形铝合金，按照所含主要合金元素和热处理状态可分为若干个系列和型号。本文选取几种典型的变形铝合金，综述了不同铝合金微观组织对转化膜成膜过程的影响，化学转化液添加剂、预处理和后处理工艺对转化膜性能的调控及作用机理，以及几种典型商业钝化剂在变形铝合金表面的应用。总结了目前变形铝合金表面锆基化学转化膜仍面临的问题和发展趋势，未来化学转化膜需在满足新型铝合金发展要求的基础上，通过不同有机、无机添加剂以及外场作用对转化膜的成膜均一性、完整性进行调控，以提高转化膜的综合性能。     

Embedded Metal Oxide Plasmonics Using Local Plasma Oxidation of AZO for Planar Metasurfaces

New methods for achieving high-quality conducting oxide metasurfaces are of great importance for a range of emerging applications from infrared thermal control coatings to epsilon-near-zero nonlinear optics. This work demonstrates the viability of plasma patterning as a technique to selectively and locally modulate the carrier density in planar Al-doped ZnO (AZO) metasurfaces without any associated topographical surface profile. This technique stands in strong contrast to conventional physical patterning which results in nonplanar textured surfaces. The approach can open up a new route to form novel photonic devices with planar metasurfaces, for example, antireflective coatings and multi-layer devices. To demonstrate the performance of the carrier-modulated AZO metasurfaces, two types of devices are realized using the demonstrated plasma patterning. A metasurface optical solar reflector is shown to produce infrared emissivity equivalent to a conventional etched design. Second, a multiband metasurface is achieved by integrating a Au visible-range metasurface on top of the planar AZO infrared metasurface. Independent control of spectral bands without significant cross-talk between infrared and visible functionalities is achieved. Local carrier tuning of conducting oxide films offers a conceptually new approach for oxide-based photonics and nanoelectronics and opens up new routes for integrated planar metasurfaces in optical technology.     

Al-Cu合金片对钢/铝异种金属激光-MIG复合焊接头组织和性能的影响

采用PLC系统控制的激光-MIG复合焊接工艺对Q890钢/6063铝合金进行异种金属焊接,研究了钢侧坡口表面添加Al-Cu合金片对接头显微组织、硬度和拉伸性能的影响。结果表明:激光-MIG复合焊接接头具有典型的熔钎焊特征;未添加Al-Cu合金片的接头界面层由舌状相Fe2Al5和粗大针状相Fe4Al13组成,厚度约18μm,添加Al-Cu合金片后由舌状相(Fe,Cu)2Al5和细小絮状相(Fe,Cu)4Al13组成,厚度约为9μm,焊缝区与热影响区的组织与未添加Al-Cu合金片时的相似;添加Al-Cu合金片的接头界面层硬度比未添加Al-Cu合金片的低约59HV;添加Al-Cu合金片的焊接接头的抗拉强度比未添加Al-Cu合金片的提高了109.8%,未添加和添加Al-Cu合金片的焊接接头均在界面层断裂。     

Flame-retardant properties and synergistic effect of ammonium polyphosphate/aluminum hydroxide/mica/silicone rubber composites

The flammability behaviors of ammonium polyphosphate/aluminum hydroxide/mica/silicone rubber (APP/Al[OH]₃/mica/SiR) ceramifying composites containing APP, Al[OH]₃, and mica are investigated by cone calorimeter test. The thermal degradation and the synergistic effect of APP/Al(OH)₃/mica/SiR composites are investigated by thermal gravimetric analysis, X-ray diffraction, scanning electron microscopy, Fourier transform infrared spectroscopy, and X-ray photoelectron spectroscopy. APP/Al(OH)₃/mica/SiR composites with 25 wt% of APP, 20 wt% of Al(OH)₃, 25 wt% of mica, and 30 wt% SiR presents a much lower total heat release, the value of peak heat release rate (PHRR), the maximum average heat release rate, the longest time to ignition, and time to the PHRR (t_PHRR), compared with the flame-retardant properties from composites with filler of APP and mica or APP and Al(OH)₃ alone. The results indicate that there is an excellent synergism in APP, Al(OH)₃, and mica, which endows APP/Al(OH)₃/mica/SiR composites with both good flame retardancy and fire prevention. The study on the synergism effect between fire prevention and flame retardancy of APP/Al(OH)₃/mica/SiR composites indicates that compounds containing P-O-Al are formed due to the reaction between APP and Al(OH)₃ during combustion in the early stage and a coherent, dense, and sealed structure is formed due to the reaction in mica, phosphates, and the thermal decomposition products of SiR during combustion in the later stage.